Iv have often wondered why a bullet sizing die couldn't be a better solution, since it would allow for a production that avoids melting metal in pots and pouring, why not just do this with dies instead?
With pure lead, shouldn't it be very easy if not easier than pouring into tiny moulds?
This is what I was referring to, isn't this what Ron Reed might be using?
http://www.swagedies.com/mm5/merchan..._Code=Specials